| Chemical Composition (wt %, max unless range given) | |||||||
|---|---|---|---|---|---|---|---|
| C | Mn | P | S | Si | Cr | Ni | Mo |
| <=0.08 | <=2.00 | <=0.045 | <=0.030 | <=1.00 | 16.0-18.0 | 10.0-14.0 | 2.00-3.00 |
| Mechanical Properties (annealed tube) | |||||
|---|---|---|---|---|---|
| Tensile Strength | Yield Strength | Elongation | Reduction of Area | Hardness | PREN |
| >=515 MPa | >=205 MPa | >=40 % | >=50 % | <=217 HB | >=24 |
| Physical Properties (typical) | ||||
|---|---|---|---|---|
| Density | Melting Point | Thermal Expansion | Thermal Conductivity | Modulus of Elasticity |
| 8.00 g/cm3 | 1375-1400 °C | 16.0 μm/m·°C | 16.3 W/m·°C | 193 GPa |
316 Stainless Steel Wire
Molybdenum-containing austenitic stainless steel wire; molybdenum significantly improves chloride ion corrosion resistance for marine safety wire and fishing leaders.
| Chemical Composition (wt %, max unless range given) | |||||||
|---|---|---|---|---|---|---|---|
| C | Mn | P | S | Si | Cr | Ni | Mo |
| <=0.08 | <=2.00 | <=0.045 | <=0.030 | <=1.00 | 16.0-18.0 | 10.0-14.0 | 2.00-3.00 |
| Mechanical Properties (annealed tube) | |||||
|---|---|---|---|---|---|
| Tensile Strength | Yield Strength | Elongation | Reduction of Area | Hardness | PREN |
| >=515 MPa | >=205 MPa | >=40 % | >=50 % | <=217 HB | >=24 |
| Physical Properties (typical) | ||||
|---|---|---|---|---|
| Density | Melting Point | Thermal Expansion | Thermal Conductivity | Modulus of Elasticity |
| 8.00 g/cm3 | 1375-1400 °C | 16.0 μm/m·°C | 16.3 W/m·°C | 193 GPa |