| Chemical Composition (wt %, max unless range given) | ||||||||
|---|---|---|---|---|---|---|---|---|
| C | Mn | P | S | Si | Cr | Ni | Mo | N |
| <=0.08 | <=2.00 | <=0.045 | <=0.030 | <=0.75 | 18.0-20.0 | 11.0-15.0 | 3.0-4.0 | <=0.10 |
| Mechanical Properties (annealed tube) | ||||
|---|---|---|---|---|
| Tensile Strength | Yield Strength | Elongation | Reduction of Area | Hardness |
| >=515 MPa | >=205 MPa | >=35 % | >=50 % | <=217 HB |
| Physical Properties (typical) | ||||
|---|---|---|---|---|
| Density | Melting Point | Thermal Expansion | Thermal Conductivity | Modulus of Elasticity |
| 8.00 g/cm3 | 1375-1400 °C | 16.0 μm/m·°C | 16.3 W/m·°C | 193 GPa |
317 Stainless Steel Wire
High-molybdenum austenitic stainless steel wire; molybdenum content higher than 316; stronger pitting and crevice corrosion resistance for chemical processing screens.
| Chemical Composition (wt %, max unless range given) | ||||||||
|---|---|---|---|---|---|---|---|---|
| C | Mn | P | S | Si | Cr | Ni | Mo | N |
| <=0.08 | <=2.00 | <=0.045 | <=0.030 | <=0.75 | 18.0-20.0 | 11.0-15.0 | 3.0-4.0 | <=0.10 |
| Mechanical Properties (annealed tube) | ||||
|---|---|---|---|---|
| Tensile Strength | Yield Strength | Elongation | Reduction of Area | Hardness |
| >=515 MPa | >=205 MPa | >=35 % | >=50 % | <=217 HB |
| Physical Properties (typical) | ||||
|---|---|---|---|---|
| Density | Melting Point | Thermal Expansion | Thermal Conductivity | Modulus of Elasticity |
| 8.00 g/cm3 | 1375-1400 °C | 16.0 μm/m·°C | 16.3 W/m·°C | 193 GPa |