| Chemical Composition (wt %, max unless range given) | |||||
|---|---|---|---|---|---|
| C | Mn | P | S | Si | Cr |
| <=0.12 | <=1.25 | <=0.060 | >=0.15 | <=1.00 | 16.0-18.0 |
| Mechanical Properties (annealed tube) | |||
|---|---|---|---|
| Tensile Strength | Yield Strength | Elongation | Hardness |
| >=450 MPa | >=205 MPa | >=20 % | <=183 HB |
| Physical Properties (typical) | ||||
|---|---|---|---|---|
| Density | Melting Point | Thermal Expansion | Thermal Conductivity | Modulus of Elasticity |
| 7.70 g/cm3 | 1425-1510 °C | 10.4 μm/m·°C | 26.0 W/m·°C | 200 GPa |
430F Stainless Steel Plate
Free-machining ferritic stainless steel plate; sulfur content increased to 0.15-0.35%; excellent machining performance for perforated plates and blanks but relatively lower corrosion resistance.
| Chemical Composition (wt %, max unless range given) | |||||
|---|---|---|---|---|---|
| C | Mn | P | S | Si | Cr |
| <=0.12 | <=1.25 | <=0.060 | >=0.15 | <=1.00 | 16.0-18.0 |
| Mechanical Properties (annealed tube) | |||
|---|---|---|---|
| Tensile Strength | Yield Strength | Elongation | Hardness |
| >=450 MPa | >=205 MPa | >=20 % | <=183 HB |
| Physical Properties (typical) | ||||
|---|---|---|---|---|
| Density | Melting Point | Thermal Expansion | Thermal Conductivity | Modulus of Elasticity |
| 7.70 g/cm3 | 1425-1510 °C | 10.4 μm/m·°C | 26.0 W/m·°C | 200 GPa |