| Chemical Composition (wt %, max unless range given) | ||||||
|---|---|---|---|---|---|---|
| Ni | Cr | Fe | C | Mn | Si | Cu |
| >=72.0 | 14.0-17.0 | 6.0-10.0 | <=0.15 | <=1.0 | <=0.5 | <=0.5 |
| Mechanical Properties (annealed tube) | |||
|---|---|---|---|
| Tensile Strength | Yield Strength | Elongation | Hardness |
| >=550 MPa | >=240 MPa | >=30 % | <=185 HB |
| Physical Properties (typical) | ||||
|---|---|---|---|---|
| Density | Melting Point | Thermal Expansion | Thermal Conductivity | Modulus of Elasticity |
| 8.43 g/cm3 | 1355-1414 °C | 13.3 μm/m·°C | 14.9 W/m·°C | 206 GPa |
Inconel 600 Nickel‑Base High‑Temperature Alloy Wire
Ni‑Cr solid‑solution‑strengthened superalloy wire with excellent high‑temperature corrosion and oxidation resistance; suitable for long‑term service below 1100°C in furnace element lead wire and thermocouple sheaths.
| Chemical Composition (wt %, max unless range given) | ||||||
|---|---|---|---|---|---|---|
| Ni | Cr | Fe | C | Mn | Si | Cu |
| >=72.0 | 14.0-17.0 | 6.0-10.0 | <=0.15 | <=1.0 | <=0.5 | <=0.5 |
| Mechanical Properties (annealed tube) | |||
|---|---|---|---|
| Tensile Strength | Yield Strength | Elongation | Hardness |
| >=550 MPa | >=240 MPa | >=30 % | <=185 HB |
| Physical Properties (typical) | ||||
|---|---|---|---|---|
| Density | Melting Point | Thermal Expansion | Thermal Conductivity | Modulus of Elasticity |
| 8.43 g/cm3 | 1355-1414 °C | 13.3 μm/m·°C | 14.9 W/m·°C | 206 GPa |