| Chemical Composition (wt %, max unless range given) | |||||||||
|---|---|---|---|---|---|---|---|---|---|
| C | Mn | P | S | Si | Cr | Ni | Mo | N | Cu |
| <=0.020 | <=1.20 | <=0.035 | <=0.020 | <=0.80 | 24.0-26.0 | 6.0-8.0 | 3.0-5.0 | 0.24-0.32 | <=0.50 |
| Mechanical Properties (annealed tube) | ||||
|---|---|---|---|---|
| Tensile Strength | Yield Strength | Elongation | Hardness | PREN |
| >=795 MPa | >=550 MPa | >=15 % | <=310 HB | >=40 |
| Physical Properties (typical) | ||||
|---|---|---|---|---|
| Density | Melting Point | Thermal Expansion | Thermal Conductivity | Modulus of Elasticity |
| 7.85 g/cm3 | 1385-1443 °C | 11.5 μm/m·°C | 17.0 W/m·°C | 200 GPa |
2507 Super Duplex Stainless Steel Bar
Super duplex stainless steel bar; higher chromium, molybdenum, and nitrogen content; extremely strong pitting and crevice corrosion resistance; strength superior to 2205; suitable for extreme corrosive environments in sub-sea tie bars.
| Chemical Composition (wt %, max unless range given) | |||||||||
|---|---|---|---|---|---|---|---|---|---|
| C | Mn | P | S | Si | Cr | Ni | Mo | N | Cu |
| <=0.020 | <=1.20 | <=0.035 | <=0.020 | <=0.80 | 24.0-26.0 | 6.0-8.0 | 3.0-5.0 | 0.24-0.32 | <=0.50 |
| Mechanical Properties (annealed tube) | ||||
|---|---|---|---|---|
| Tensile Strength | Yield Strength | Elongation | Hardness | PREN |
| >=795 MPa | >=550 MPa | >=15 % | <=310 HB | >=40 |
| Physical Properties (typical) | ||||
|---|---|---|---|---|
| Density | Melting Point | Thermal Expansion | Thermal Conductivity | Modulus of Elasticity |
| 7.85 g/cm3 | 1385-1443 °C | 11.5 μm/m·°C | 17.0 W/m·°C | 200 GPa |