| Chemical Composition (wt %, max unless range given) | |||||||
|---|---|---|---|---|---|---|---|
| C | Mn | P | S | Si | Cr | Ni | N |
| <=0.15 | <=2.00 | <=0.045 | <=0.030 | <=1.00 | 16.0-18.0 | 6.0-8.0 | <=0.10 |
| Mechanical Properties (annealed tube) | ||||
|---|---|---|---|---|
| Tensile Strength | Yield Strength | Elongation | Reduction of Area | Hardness |
| >=515 MPa | >=205 MPa | >=40 % | >=50 % | <=217 HB |
| Physical Properties (typical) | ||||
|---|---|---|---|---|
| Density | Melting Point | Thermal Expansion | Thermal Conductivity | Modulus of Elasticity |
| 7.93 g/cm3 | 1399-1421 °C | 17.0 μm/m·°C | 16.2 W/m·°C | 193 GPa |
301 Stainless Steel Bar
Cr-Ni high-strength austenitic stainless steel bar; work-hardens rapidly; extremely high strength through cold drawing for precision lead-screws and drive shafts.
| Chemical Composition (wt %, max unless range given) | |||||||
|---|---|---|---|---|---|---|---|
| C | Mn | P | S | Si | Cr | Ni | N |
| <=0.15 | <=2.00 | <=0.045 | <=0.030 | <=1.00 | 16.0-18.0 | 6.0-8.0 | <=0.10 |
| Mechanical Properties (annealed tube) | ||||
|---|---|---|---|---|
| Tensile Strength | Yield Strength | Elongation | Reduction of Area | Hardness |
| >=515 MPa | >=205 MPa | >=40 % | >=50 % | <=217 HB |
| Physical Properties (typical) | ||||
|---|---|---|---|---|
| Density | Melting Point | Thermal Expansion | Thermal Conductivity | Modulus of Elasticity |
| 7.93 g/cm3 | 1399-1421 °C | 17.0 μm/m·°C | 16.2 W/m·°C | 193 GPa |