| Chemical Composition (wt %, max unless range given) | |||||||
|---|---|---|---|---|---|---|---|
| C | Mn | P | S | Si | Cr | Ni | Ti |
| <=0.08 | <=2.00 | <=0.045 | <=0.030 | <=1.00 | 17.0-19.0 | 9.0-12.0 | >=5×(C+N) and <=0.70 |
| Mechanical Properties (annealed tube) | ||||
|---|---|---|---|---|
| Tensile Strength | Yield Strength | Elongation | Reduction of Area | Hardness |
| >=515 MPa | >=205 MPa | >=40 % | >=50 % | <=217 HB |
| Physical Properties (typical) | ||||
|---|---|---|---|---|
| Density | Melting Point | Thermal Expansion | Thermal Conductivity | Modulus of Elasticity |
| 8.03 g/cm3 | 1398-1446 °C | 16.7 μm/m·°C | 16.2 W/m·°C | 193 GPa |
321 Stainless Steel Bar
Titanium-stabilized austenitic stainless steel bar; titanium fixes carbon atoms; prevents intergranular corrosion; suitable for medium-high temperature turbine blades and afterburner pins.
| Chemical Composition (wt %, max unless range given) | |||||||
|---|---|---|---|---|---|---|---|
| C | Mn | P | S | Si | Cr | Ni | Ti |
| <=0.08 | <=2.00 | <=0.045 | <=0.030 | <=1.00 | 17.0-19.0 | 9.0-12.0 | >=5×(C+N) and <=0.70 |
| Mechanical Properties (annealed tube) | ||||
|---|---|---|---|---|
| Tensile Strength | Yield Strength | Elongation | Reduction of Area | Hardness |
| >=515 MPa | >=205 MPa | >=40 % | >=50 % | <=217 HB |
| Physical Properties (typical) | ||||
|---|---|---|---|---|
| Density | Melting Point | Thermal Expansion | Thermal Conductivity | Modulus of Elasticity |
| 8.03 g/cm3 | 1398-1446 °C | 16.7 μm/m·°C | 16.2 W/m·°C | 193 GPa |