| Chemical Composition (wt %, max unless range given) | ||||||
|---|---|---|---|---|---|---|
| C | Mn | P | S | Si | Cr | N |
| <=0.20 | <=1.50 | <=0.040 | <=0.030 | <=1.00 | 23.0-27.0 | <=0.25 |
| Mechanical Properties (annealed tube) | |||
|---|---|---|---|
| Tensile Strength | Yield Strength | Elongation | Hardness |
| >=515 MPa | >=275 MPa | >=20 % | <=217 HB |
| Physical Properties (typical) | ||||
|---|---|---|---|---|
| Density | Melting Point | Thermal Expansion | Thermal Conductivity | Modulus of Elasticity |
| 7.65 g/cm3 | 1425-1510 °C | 10.4 μm/m·°C | 21.8 W/m·°C | 200 GPa |
446 Stainless Steel Bar
High-chromium ferritic stainless steel bar; chromium content 23-30%; oxidation resistance up to 1100°C; excellent high-temperature corrosion resistance for burner tips and kiln furniture legs.
| Chemical Composition (wt %, max unless range given) | ||||||
|---|---|---|---|---|---|---|
| C | Mn | P | S | Si | Cr | N |
| <=0.20 | <=1.50 | <=0.040 | <=0.030 | <=1.00 | 23.0-27.0 | <=0.25 |
| Mechanical Properties (annealed tube) | |||
|---|---|---|---|
| Tensile Strength | Yield Strength | Elongation | Hardness |
| >=515 MPa | >=275 MPa | >=20 % | <=217 HB |
| Physical Properties (typical) | ||||
|---|---|---|---|---|
| Density | Melting Point | Thermal Expansion | Thermal Conductivity | Modulus of Elasticity |
| 7.65 g/cm3 | 1425-1510 °C | 10.4 μm/m·°C | 21.8 W/m·°C | 200 GPa |