| Chemical Composition (wt %, max unless range given) | |||||||
|---|---|---|---|---|---|---|---|
| C | Mn | P | S | Si | Cr | Ni | Mo |
| <=0.12 | 14.0-16.0 | <=0.045 | <=0.030 | 0.30-1.00 | 17.0-18.5 | >=1.00 | >=0.35 |
| Mechanical Properties (annealed tube) | |||
|---|---|---|---|
| Tensile Strength | Yield Strength | Elongation | Hardness |
| >=620 MPa | >=310 MPa | >=40 % | <=217 HB |
| Physical Properties (typical) | ||||
|---|---|---|---|---|
| Density | Melting Point | Thermal Expansion | Thermal Conductivity | Modulus of Elasticity |
| 7.93 g/cm3 | 1398-1453 °C | 17.5 μm/m·°C | 16.2 W/m·°C | 195 GPa |
XM-31 Stainless Steel Bar
Ultra-high manganese austenitic stainless steel bar; manganese content 14-16%; unique mechanical properties and work-hardening characteristics for crusher jaws and railway crossing components.
| Chemical Composition (wt %, max unless range given) | |||||||
|---|---|---|---|---|---|---|---|
| C | Mn | P | S | Si | Cr | Ni | Mo |
| <=0.12 | 14.0-16.0 | <=0.045 | <=0.030 | 0.30-1.00 | 17.0-18.5 | >=1.00 | >=0.35 |
| Mechanical Properties (annealed tube) | |||
|---|---|---|---|
| Tensile Strength | Yield Strength | Elongation | Hardness |
| >=620 MPa | >=310 MPa | >=40 % | <=217 HB |
| Physical Properties (typical) | ||||
|---|---|---|---|---|
| Density | Melting Point | Thermal Expansion | Thermal Conductivity | Modulus of Elasticity |
| 7.93 g/cm3 | 1398-1453 °C | 17.5 μm/m·°C | 16.2 W/m·°C | 195 GPa |